K-FLEX 148
Viscosity @ 25°C 3,750 cPsHydroxyl Number 235Equivalent Weight, g/eq. (as supplied) 238Polyester diolLower viscosity version of K-FLEX 188. Improves flexibility and gloss. Good flow and leveling. Excellent intercoat adhesion. Recommended for primers. -
K-FLEX 171-90
Viscosity @ 25°C 3,700 cPsHydroxyl Number 122Equivalent Weight, g/eq. (as supplied) 432Polyester diolChain extended version of K-FLEX 188 with improved adhesion and flexibility. Low crosslinker demand. -
K-FLEX 188
Viscosity @ 25°C 10,000 cPsHydroxyl Number 230Equivalent Weight, g/eq. (as supplied) 244Polyester diolMost versatile polyester diol. Improves flexibility while maintaining hardness. Also improves salt spray, humidity resistance and exterior durability. Highly recommended for 2k PU. -
K-FLEX A307
Viscosity @ 25°C 5,400 cPsHydroxyl Number 140Equivalent Weight, g/eq. (as supplied) 400Polyester diolLow viscosity, 100% solids. Improves flexibility. Low crosslinker demand. Recommended for isocyanate and aminoplast systems. -
K-FLEX A308
Viscosity @ 25°C 1,500 cPsHydroxyl Number 260Equivalent Weight, g/eq. (as supplied) 216Polyester diolLow viscosity, providing good hardness and adhesion while lowering VOCs. Recommended for acrylic/isocyanate and acrylic/melamine systems. -
K-FLEX UD-320
Viscosity @ 25°C 7,000 cPsHydroxyl Number 300% Active 82Urethane diolIncorporation of urethane into HMMM type systems without use of NCO. Increases application solids and hardness. Improves chemical resistance, exterior durability and hydrolytic stability. -
K-FLEX UD-320-100
Viscosity @ 50°C 7,000 cPsHydroxyl Number 350% Active 100Urethane diolRecommended for prepolymer synthesis and 100% solids WB/SB melamine crosslinked systems or 2K PU. Used for preparation of polyester polyurethanes or alkyd polyurethanes. Provides hardness and exterior durability -
K-FLEX UD-350W
Viscosity @ 25°C 4,000 cPs% Active 88Hydroxyl Number 300Urethane diolHigh solids, low viscosity aqueous urethane diol resin that increases hardness and provides improved resistance properties in WB/WR 2-component polyurethane -
K-FLEX XM-3018
Company Division CoatingsMarket Application 2K PUApplication Advantage Ambient curePolyester diolHydrolytically stable, water-reducible polyester polyol resin modifier that enhances durability, appearance, and performance. -
K-FLEX XM-332
Viscosity @ 25°C 400 cPsHydroxyl Number 265Equivalent Weight, g/eq. (as supplied) 212Polyester diolLowest viscosity polyester diol that produces the softest films. Provides abrasion resistance, scratch resistance and good weatherability. -
K-FLEX XM-337
Viscosity @ 25°C 55,000 cPsHydroxyl Number 220Equivalent Weight, g/eq. (as supplied) 260Polyester diolImproves flexibility, impact resistance and chemical resistance. Excellent UV durability. Recommended for urethane and blocked isocyanate systems. -
K-FLEX XM-359
Viscosity @ 25°C 9,800 cPsHydroxyl Number 230Equivalent Weight, g/eq. (as supplied) 244Polyester diolLonger pot life version of K-FLEX 188. Improves flexibility while maintaining hardness. Also improves salt spray, humidity resistance and exterior durability. Highly recommended for 2k PU. -
K-FLEX XM-B301
Viscosity @ 25°C 1,100 cPsHydroxyl Number 190Application Advantage AdhesionAcetoacetate reactive diluentPrimarily recommended for use in epoxy/polyamide primers, but can also be used in systems crosslinked with amino resins or polyisocyanates.